RESUMO
ABSTRACT Objective: The aim of this study is to analyze if both color and nylon fibers have an influence on microwave-cured acrylic resin properties. Methods: Rectangular and disk-shaped specimens were prepared using acrylic resins; medium pink with and without nylon fibers and colorless without nylon fibers. To obtain the rectangular specimens, a stainless steel die was used with the following dimensions: 64 X 10 x 3 mm (± 0.5mm). To obtain disk-shaped specimens, a die 50mm (±0.5mm) in diameter and 0.5mm (±0.05mm) thick was employed. They were randomized to form groups: control (colorless acrylic) and experimental (medium pink, with and without nylon fibers), with each group consisting of ten (10) specimens rectangular in shape and five (5) disk-shaped. They were analyzed in six (6) assays (izod impact strength, n=10; Knoop hardness, n=10; glass transition temperature, n=3; water sorption and solubility, n=5; degree of monomer/polymer conversion, n=1; flexural strength and flexural modulus, n=10). All variables were subjected to the analysis of variance test followed by Tukey's multiple comparison test, at a 5% level of significance. Results: The analysis of the monomer/polymer degree of conversion did not reveal any difference between the three groups of resins (medium pink, with and without nylon fibers and colorless resin); it was approximately 88%. The results did not show significant differences between the groups for each variable (p>0.05). Conclusion: The results showed that color and presence of nylon fibers in acrylic resins did not affect the properties analyzed in this study.
RESUMO Objetivo: Analisar se corantes e fibras de nylon influenciam nas propriedades de uma resina acrílica ativada por energia de micro-ondas. Métodos: Espécimes retangulares e em forma de disco foram confeccionados em resina acrílica rosa médio com e sem fibras de nylon e incolor sem fibras. Para obter os espécimes retangulares, foi utilizada uma matriz de aço inoxidável com as seguintes dimensões: 64 X 10 X 3 (± 0,5mm) e para obter os espécimes em forma de disco, foi utilizada uma matriz com 50mm (± 0,5mm) de diâmetro e 0,5mm (±0,05mm) de espessura. Os mesmos foram randomizados para formar os grupos controle (acrílico incolor sem fibras) e experimentais (rosa médio com e sem fibras), sendo cada grupo composto por dez (10) espécimes retangulares e cinco (5) em forma de disco. Foram os mesmos então submetidos a seis (6) ensaios (resistência ao impacto izod, n=10; dureza knoop, n=10; temperatura de transição vítrea, n=3; sorção e solubilidade, n=5; grau de conversão, n=1; resistência à flexão e módulo de flexão, n=10). Todas as variáveis foram submetidas à análise de variância seguida pelo teste de comparações múltiplas de Tukey, com nível de significância de 5%. Resultados: O grau de conversão foi de 88% para os 3 grupos de resinas e os resultados não mostraram diferença estatisticamente significativa entre os mesmos para cada variável (p>0,05). Conclusão: Os resultados mostraram que o corante e a presença de fibras de nylon em resina acrílica não afetaram as propriedades analisadas nesse estudo.
RESUMO
Objective: The objective of this study was to evaluate the effectiveness of disinfection methods in microwave and immersion in peracetic acid in heat-cured, self-cured and microwave-cured acrylic resin, contaminated with Candida albicans.Methods: Five specimens were prepared for each type of acrylic resin. All were infected with Candida Albicans, incubated at 37°C for 24 hours. The group which underwent microwave energy was irradiated with a power of 840W for 1 minute and the other group underwent disinfection by soaking of 0.2% peracetic acid for 5 minutes.Results: All samples proved to be contaminated after the incubation period. After the different processes of disinfection, both immersion in 0.2% peracetic acid as microwave irradiation were effective in disinfection of the 3 types of acrylic resins contaminated by Candida Albicans.Conclusion: Concluded that soaking in 0,2% peracetic acid for 5 minutes with microwave irradiation power 840W for 1 minute are effective methods for disinfecting heat-cured acrylic resin, self-cured acrylic resin and microwave-cured acrylic resin, contaminated with Candida Albicans.
Objetivo: Avaliar a eficácia dos métodos de desinfecção em microondas e imersão em ácido peracético em resina acrílica termopolimerizável, autopolimerizável e resina acrílica polimerizada por microondas, contaminadas com Candida albicans.Métodos: Cinco amostras foram preparadas para cada tipo de resina acrílica. Todas foram infectadas com Candida Albicans, incubadas a 37 ° C durante 24 h. O grupo submetido a energia de microondas foi irradiada com uma potência de 840W durante 1 minuto e o outro grupo foi submetido a desinfecção por imersão de ácido peracético a 0,2% durante 5 minutos.Resultados: Todas as amostras mostraram estar contaminadas depois do período de incubação. Depois dos diferentes processos de desinfecção, tanto a imersão em 0,2% de ácido peracético, como a irradiação de microondas foram eficazes na desinfecção dos 3 tipos de resinas acrílicas contaminados por Candida Albicans.Conclusão: Concluiu-se que a imersão em ácido peracético 0,2% durante 5 minutos e a irradiação de microondas com potência de 840W durante 1 minuto são métodos eficazes para a desinfecção de resina acrílica termopolimerizável, resina acrílica autopolimerizável e resina acrílica polimerizada por microondas, contaminados com Candida Albicans.
RESUMO
Pra a obtençäo do melhor desempenho do gesso odontológico é necessário que se obedeça uma relaçäo água/pó adequada a fim de manter suas propriedades ideais. A medida mais precisa de pó de gesso é tradicionalmente obtida através de uma balança, o que, clinicamente, acaba näo sendo um método muito prático e rápido. Na tentativa de encontrar uma alternativa para substituir a balança foi proposta uma técnica de compactaçäo do pó de gesso utilizando uma medida volumétrica. Essa técnica consiste em introduzir dentro do saco de gesso um medidor, o qual é segurado por uma das mäos, enquanto que a palma da outra, pressiona a superfície do medidor, que é apoiado pela parte ventral dos dedos desta mäo. Esse procedimento pressupöe três compactaçöes para cada operador, obtendo-se daí uma média da massa compactada. Cada um dos dez operadores reproduziu por seis vezes o referido procedimento, obtendo-se entäo uma média final para cada operador. As massas resultantes de cada operaçäo, de cada operador foram pesadas e os resultados comparados por testes estatísticos evidenciaram a existência de uma diferença estatísticamente significativa (p=0,006) entre os operadores